Luhur Alumina Refractory Castable
Émbaran produk
| Ngaran Produk | Refractory Castable |
| Kategori | Semén Low Castable/Kakuatan Tinggi Castable/Luhur Alumina Castable / Lightweight Castable |
| Komposisi | agrégat refractory, bubuk jeung binders |
| Fitur | 1. Gampang Pangwangunan, 2.Alus Slag Résistansi, 3.Alus Résistansi Korosi, 4. Good Résistansi Seuneu, 5.Energy Saving Jeung Protection Lingkungan. |
| Aplikasi | loba dipaké dina rupa-rupa tungku industri suhu luhur. |
| Produk | Low semén Castable | Kakuatan Luhur Castable |
| Katerangan | Castables semén low nujul kana castables anyar kalawan saeutik pisan map semén.Eusi semén tina castables refractory umumna 15% nepi ka 20%, sarta eusi semén tina castables semén low nyaeta ngeunaan 5%, sarta sababaraha malah diréduksi jadi 1% nepi ka 2%. | Kakuatan anu tahan tahan castable diwangun ku agrégat kakuatan tinggi, campuran mineral, agrégat kakuatan tinggi sareng anti retakan sareng agén tahan ngagem. |
| Fitur | Résistansi shock termal, résistansi slag, sareng résistansi erosi ningkat sacara signifikan, ngalangkungan bata refractory anu sami. | kakuatan tinggi, résistansi maké tinggi, résistansi dampak, résistansi erosi, perméabilitas anti minyak, kontrol bentuk sawenang, integritas kuat, konstruksi basajan, kinerja konstruksi alus, sarta layanan panjang. |
| Aplikasi | 1.Lining rupa tungku perlakuan panas, furnaces pemanasan, kilns aci, kilns usaha Rotary, tungku listrik nyertakeun, blast tungku tapholes; 2.Self-ngalir low-semén castables anu cocog pikeun-suhu luhur semprot gun linings pikeun metallurgy semprot jeung réaktor cracking katalitik pétrokimia Ngagem-tahan, pinding luar tungku pemanasan pipa cai-tiis, jsb. | Lapisan tahan aus lapisan slag sluice,palung bijih, spout batubara, hopper sareng silo dina metalurgi, batubara, kakuatan termal, kimia,semén jeung industri lianna, sarta blast tungku Pergaulan silo, sintering silo, feeder, pelletizer, jsb. |
| Produk | Luhur Alumina Castable | Ringan Castable |
| Katerangan | Castables-alumina tinggi anu refractorycastables dijieunna tina bahan baku luhur-aluminasalaku agrégat jeung powders, sarta ditambahkeunkalawan binders. | The castable lightweight kalawan dénsitas bulk low dijieunna tina semén aluminate, bahan halus alumina tinggi, ceramsite, sarta aditif. |
| Fitur | Mibanda kakuatan mékanis tinggi jeung résistansi shock termal alus, résistansi abrasion jeung pasipatan lianna. | Kapadetan bulk low, konduktivitas termal leutik, pangaruh insulasi termal alus, kakuatan compressive tinggi, asam jeung résistansi korosi gas asam, insulasi panas, insulasi termal, sarta nyerep cai low. |
| Aplikasi | Ieu utamana dipaké salaku pinding jero boilers, blast tungku kompor blast panas, furnaces pemanasan, kilns keramik jeung kilns lianna. | The castable lightweight bisa dipaké pikeun lapisan insulasi termal tina tungku industri suhu luhur jeung alat ogé dipaké pikeun pinding rupa-rupa pipa gas suhu luhur. |
Indéks Produk
Panas Blast Kompor
Torowongan Kiln
Rotary Kiln
Industri beusi jeung baja: utamana dipaké pikeun pangropéa sarta patching of furnaces arc listrik, steelmaking furnaces, ladles jeung alat lianna.
Industri logam non-ferrous: dipaké pikeun patching na repairing tambaga, aluminium, séng, nikel jeung tungku smelting non-ferrous séjén sarta converters.
Industri kaca: dipaké pikeun pangropéa sarta patch karya furnaces kaca, furnaces annealing jeung alat lianna.
| Ngaran Produk | Low semén Castable | |||||
| INDEKS | RBTZJ-42 | RBTZJ-60 | RBTZJ-65 | RBTZJS-65 | RBTZJ-70 | |
| Suhu Wates Gawé | 1300 | 1350 | 1400 | 1400 | 1450 | |
| Kapadetan Bulk (g/cm3)110 ℃ × 24h ≥ | 2.15 | 2.3 | 2.4 | 2.4 | 2.45 | |
| Kakuatan Bending tiis110 ℃ × 24h (MPa) ≥ | 4 | 5 | 6 | 6 | 7 | |
| Tiis Crushing Kakuatan (MPa) ≥ | 110 ℃ × 24h | 25 | 30 | 35 | 35 | 40 |
| CT ℃ × 3 jam | 50 1300 ℃ × 3h | 55 1350 ℃ × 3h | 60 1400 ℃ × 3h | 40 1400 ℃ × 3h | 70 1400 ℃ × 3h | |
| Robah Linier Permanén@CT℃×3h(%) | -0,5 ~ + 0,5 1300 ℃ | -0,5 ~ + 0,5 1350 ℃ | 0~+0.8 1400 ℃ | 0~+0.8 1400 ℃ | 0~+1.0 1400 ℃ | |
| Résistansi Shock Termal (1000 ℃ cai) ≥ | ― | ― | ― | 20 | ― | |
| Al2O3(%) ≥ | 42 | 60 | 65 | 65 | 70 | |
| CaO(%) ≤ | 2-3 | 2-3 | 2-3 | 2-3 | 2-3 | |
| Fe2O3(%) ≤ | 2.0 | 1.5 | 1.5 | 1.5 | 1.5 | |
| Ngaran Produk | Kakuatan Luhur Castable | |||||
| INDEKS | HS-50 | HS-60 | HS-70 | HS-80 | HS-90 | |
| Suhu wates gawé (℃) | 1400 | 1500 | 1600 | 1700 | 1800 | |
| 110 ℃ Bulk Density (g / cm3) ≥ | 2.15 | 2.30 | 2.40 | 2.50 | 2.90 | |
| Modulus Pecah (MPa) ≥ | 110 ℃ × 24h | 6 | 8 | 8 | 8.5 | 10 |
| 1100 ℃ × 3h | 8 | 8.5 | 8.5 | 9 | 9.5 | |
| 1400 ℃ × 3h | 8,5 1300 ℃ × 3h | 9 | 9.5 | 10 | 15 | |
| Tiis Crushing Kakuatan (MPa) ≥ | 110 ℃ × 24h | 35 | 40 | 40 | 45 | 60 |
| 1100 ℃ × 3h | 40 | 50 | 45 | 50 | 70 | |
| 1400 ℃ × 3h | 45 1300 ℃ × 3h | 55 | 50 | 55 | 100 | |
| Robah Linier Permanén(%) | 1100 ℃ × 3h | -0.2 | -0.2 | -0.25 | -0.15 | -0.1 |
| 1400 ℃ × 3h | -0,45 1300 ℃ × 3h | -0.4 | -0.3 | -0.3 | -0.1 | |
| Al2O3(%) ≥ | 48 | 48 | 55 | 65 | 75 | 90 |
| CaO(%) ≤ | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 |
| Fe2O3(%) ≤ | 3.5 | 3.5 | 3.0 | 2.5 | 2.0 | 2.0 |
| Ngaran Produk | Luhur Alumina Castable | ||||||
| INDEKS | Al2O3(%)≥ | CaO(%)≥ | Refractoriness (℃) | CT ℃ × 3h PLC ≤1% | 110 ℃ Saatos Garing (MPa) | ||
| CCS | MOR | ||||||
| Liat kabeungkeut | NL-45 | 45 | ― | 1700 | 1350 | 8 | 1 |
| NL-60 | 60 | ― | 1720 | 1400 | 9 | 1.5 | |
| NL-70 | 70 | ― | 1760 | 1450 | 10 | 2 | |
| Semén kabeungkeut | GL-42 | 42 | ― | 1640 | 1350 | 25 | 3.5 |
| GL-50 | 50 | ― | 1660 | 1400 | 30 | 4 | |
| GL-60 | 60 | ― | 1700 | 1400 | 30 | 4 | |
| GL-70 | 70 | ― | 1720 | 1450 | 35 | 5 | |
| GL-85 | 85 | ― | 1780 | 1500 | 35 | 5 | |
| Low semén kabeungkeut | DL-60 | 60 | 2.5 | 1740 | 1500 | 30 | 5 |
| DL-80 | 80 | 2.5 | 1780 | 1500 | 40 | 6 | |
| Kabeungkeut fosfat | LL-45 | 45 | ― | 1700 | 1350 | 20 | 3.5 |
| LL-60 | 60 | ― | 1740 | 1450 | 25 | 4 | |
| LL-75 | 75 | ― | 1780 | 1500 | 30 | 5 | |
| Natrium Silikat kabeungkeut | BL-40 | 40 | ― | ― | 1000 | 20 | ― |
| Ngaran Produk | Ringan Castable | ||||||
| Suhu wates gawé | 1100 | 1200 | 1400 | 1500 | 1600 | ||
| 110 ℃ Bulk Density (g / cm3) ≥ | 1.15 | 1.25 | 1.35 | 1.40 | 1.50 | ||
| Modulus Pecah (MPa) ≥ | 110 ℃ × 24h | 2.5 | 3 | 3.3 | 3.5 | 3.0 | |
| 1100 ℃ × 3h | 2 | 2 | 2.5 | 3.5 | 3.0 | ||
| 1400 ℃ × 3h | ― | ― | 3 | 10.8 | 8.1 | ||
| Kakuatan Ngarecah Tiis (MPa) ≥ | 110 ℃ × 24h | 8 | 8 | 11 | 12 | 10 | |
| 1100 ℃ × 3h | 4 | 4 | 5 | 11 | 10 | ||
| 1400 ℃ × 3h | ― | ― | 15 | 22 | 14 | ||
| Robah Linier Permanén(%) | 1100 ℃ × 3h | -0,65 1000 ℃ × 3h | -0.8 | -0.25 | -0.15 | -0.1 | |
| 1400 ℃ × 3h | ― | ― | -0.8 | -0.55 | -0.45 | ||
| Konduktivitas termal (W/mk) | 350 ℃ | 0.18 | 0.20 | 0.30 | 0.48 | 0.52 | |
| 700 ℃ | 0.25 | 0.25 | 0.45 | 0.61 | 0.64 | ||
| Al2O3(%) ≥ | 33 | 35 | 45 | 55 | 65 | ||
| Fe2O3(%) ≤ | 3.5 | 3.0 | 2.5 | 2.0 | 2.0 | ||
Aplikasi